Borates: A "New" Flux for Glossy Glazes

New research shows that borates can maintain the quality of a sanitaryware glaze through several re-fires-ensuring a glossy, hygienic final product.

Photo courtesy of U.S. Borax and Kohler Co.

Wash basins, water closets, toilets and other sanitaryware and plumbing products comprise one of the largest examples of glazed ceramics that most of us encounter. These practical and often attractive fixtures can be complex, with intertwining void spaces and conduits that must be kept hygienic. Both factors have always been a challenge to manufacturers.

Many years ago, sanitaryware and plumbing products were produced in a traditional two-firing process-the first fire to harden the clay body and the second to vitrify the glaze. However, re-firing large, complex shapes was expensive, labor-intensive and energy-inefficient, and it yielded a low production rate.

The double-fire process eventually gave way to single-fire. Single firing produces a better article at a lower cost but is a much more difficult process. The glaze is applied to the dry but raw clay body. Both have to mature together, a process that can take between 12 and 20 hours at temperatures rising to 1250°C (2280°F). The glaze must both develop a glossy surface and remain "open" (gas permeable) long enough to allow the body to mature and de-gas without causing bubble-related defects. If such defects occur, they announce themselves only when the piece appears from the kiln finished and glazed, but unready for the market-not necessarily scrap, but in need of treatment.

A manufacturer can congratulate itself if its reject rate is only 25%. Sometimes the reject rate can be as high as 60% if best-quality pieces are the goal. Glazes often have iron speckling from conveyor or kiln contamination, "crawling" where there is incomplete coverage, or body pinholes visible as holes in the glaze. The article must then be sent back to the kiln for defect treatment, sometimes more than once. Some top-quality manufacturers re-fire up to three times to achieve the desired result, and sometimes the piece has to be completely re-glazed.

The problem with this process is not just the extra time, money and energy used. Since re-firing is usually at a slightly lower temperature (by 50-100°C or 122-212°F), devitrification of the glaze often occurs. This means that crystals form and dull the surface, lowering the piece's quality. More re-firing equates to less gloss, a rougher surface, lower quality, and worse, a less hygienic product.

Borate Benefits

First-fire quality problems will no doubt continue due to the nature of the items in production. But research has shown that if borate is added to the glaze mixture, the glaze quality remains consistently high even through several re-fires because it prevents devitrification from occurring.

Boric oxide is well known to glaze technologists as being a multifunctional batch ingredient with many useful properties. However, in sanitaryware, in which a raw glaze is used, the solubility of many common borates has meant that they have been discounted in spite of their potential benefits. Equally, they have sometimes been suspected of promoting glaze bubbling at the temperatures used.

Insoluble borates (borates that have minimal solubility in water), on the other hand, don't contribute any negative effects. Such borates are available as frits, calcium borates and zinc borates, and all are custom-made to avoid devitrification problems.

Using advanced computer modeling techniques and laboratory tests substantiated by a leading U.K. industry association, researchers have confirmed that including borates in the glaze in exactly the right amount deals with the devitrification problem, and does not cause glaze bubbling. (See sidebar: Experimental Glaze Development Using Borates.)

The glaze glossiness, measured in the laboratory after the first firing, was slightly less than the standard glaze, but the difference was imperceptible to the eye. In subsequent re-firings, virtually no reduction of gloss occurs. In contrast, the gloss of a non-borate glaze will have fallen by almost 40% after three re-fires. Additionally, only a very small percentage (2% by weight) of B2O3 was needed in the batch to produce these benefits.

Use of borates also provides good high-temperature fluxing, replacing the need for barium and zinc oxides. Borate glazes also result in far better chemical resistance in this notoriously harsh environment. And perhaps most importantly for most manufacturers, recent work at Rutger's University in New Brunswick, N.J., has demonstrated that highly significant cost savings can be won by the use of borates. By being able to avoid the need for other batch ingredients, the cost of the glaze can fall by up to 25%.

Overcoming Obstacles

By including borates in raw sanitaryware glazes, many of the former obstacles presented by solubility issues can be overcome. Borates can offer increased flexibility in glaze formulation and properties, and can also help increase production efficiency in manufacturing. Additionally, the improved chemical durability and devitrification resistance of borate-containing glazes can provide a smoother glaze surface-ensuring a glossy, hygienic final product.

For More Information

For more information about using borates in sanitaryware glazes, contact U.S. Borax Inc., 26877 Tourney Road, Valencia, CA 91355-1847; (661) 287-5400; fax (661) 287-5495.

SIDEBAR: Experimental Glaze Development Using Borates

A standard industrial white boric oxide (B2O3)-free glaze composition was taken, and computer models of glass properties were used to include B2O3. The other oxides were adjusted so that the calculated properties of the glaze remained the same (viscosity, softening point, thermal expansion) (see Table 1).

Glaze Preparation and Evaluation. Glazes were ball-milled (62.5 wt.% solids, 1% CMC binder) to a particle size of about 70% < 10 micrometers and sprayed onto bisque tiles and sanitaryware to a (dry) weight of 1.25 kg/m2, which corresponds to a fired thickness of 0.5 mm. First firings used a heating rate of 100°C per hour and a peak temperature of 1200°C per minute followed by natural cooling. Re-firings used the same cycle with a peak of 1100°C.

The glaze properties of interest were gloss (first fire and re-fire), sealing temperature and liquidus temperature (the temperature below which devitrification occurs). Gloss was measured with a 60° gloss meter, and sealing temperature was measured by firing a glazed bisque tile in a gradient furnace and then impregnating the piece with a blue dye. Liquidus temperature was measured by placing strips of glazed and fired bisque in a gradient furnace for two hours. The sample was then examined visually and with a reflected light optical microscope to detect any devitrification. These tests were repeated on sanitaryware body slabs using the best glazes from the tile experiments.



Increasing the boron content caused the first fire gloss to decrease, but the change was imperceptible, and all first fire glazes were similar in appearance. (A change in gloss of greater than three units is visible to the naked eye.) On re-firing, however, the boron-free glaze devitrified, particularly on the second and third re-fire. The gloss of the 4% B2O3 glaze changed on re-firing-in some samples, the surface became disrupted by pinholes. The 2% glaze did not change its appearance, and after two re-fires was identical to the first firing. (Boron-containing glazes were not re-fired a third time.) (See Figure 1.)

Sealing and Liquidus Temperature

Adding 2% boric oxide reduced the sealing temperature by 40 to 55µC, while 4% boric oxide reduced the sealing temperature an additional 35 to 65°C. Adding B2O3 also reduced the liquidus temperature, which reduces the chance of devitrification on re-firing. Glazes with no B2O3 showed severe devitrification, with many large crystals visible to the naked eye. Adding 2% B2O3 reduced the devitrification so that only a slight amount could be seen, and only under a microscope. No crystallisation occurred with 4% B2O3.


The standard glaze and B2O3-containing glazes were evaluated for resistance to chemical attack (50% HCl, 10% acetic acid, Teepol, 5% NaOh, 3% H2SO4, 10% citric acid, 0.15% Na-stearate) and staining and burning, both before and after re-firing. The first fire glazes were also subjected to craze resistance testing. All samples passed the tests. An additional chemical durability test was performed by immersion in an alkaline detergent (0.4% IEC 436 solution at 77°C for 32 hours). This showed differences between the glazes-the standard was badly attacked, the calcium borate-containing glaze was slightly attacked, and the glaze made with the high boron content frit was unaffected. The presence of boric oxide in the glaze therefore significantly improves the resistance to chemical attack by alkaline detergents.

Zinc and calcium borates and high-boron content frits...

  • act as a flux, initiating glass formation in early melting stages
  • reduce liquidus temperature-necessary to stop devitrification
  • reduce viscosity
  • reduce surface tension
  • lower sealing and maturing temperatures, leading to glazes with smoother finishes
  • reduce thermal expansion to that of the body
  • improve glaze luster
  • increase mechanical strength and scratch resistance
  • improve durability against aqueous and chemical attack

Did you enjoy this article? Click here to subscribe to Ceramic Industry Magazine.

You must login or register in order to post a comment.



Image Galleries

2015 Ceramics Expo

Snapshots from the 2015 Ceramics Expo, April 28-30, Cleveland, Ohio. Posted: May 14, 2015.


Ceramics Expo podcast
Editor Susan Sutton discusses the upcoming Ceramics Expo with event director Adam Moore.
More Podcasts

Ceramic Industry Magazine

CI May 2015 cover

2015 May

Our May issue covers bulk batching, pneumatic conveyors, high-temperature furnaces and more! Be sure to check it out today.

Table Of Contents Subscribe

Daily News

We know where you find the latest ceramic industry news (ahem), but where do you catch up on the rest of your daily news?
View Results Poll Archive


M:\General Shared\__AEC Store Katie Z\AEC Store\Images\Ceramics Industry\handbook of advanced ceramics.gif
Handbook of Advanced Ceramics Machining

Ceramics, with their unique properties and diverse applications, hold the potential to revolutionize many industries, including automotive and semiconductors.

More Products

Clear Seas Research

Clear Seas ResearchWith access to over one million professionals and more than 60 industry-specific publications,Clear Seas Research offers relevant insights from those who know your industry best. Let us customize a market research solution that exceeds your marketing goals.


facebook_40px twitter_40px  youtube_40pxlinkedin_40google+ icon 40px


CI Data Book July 2012

Ceramic Industry's Directories including Components, Equipment Digest, Services, Data Book & Buyers Guide, Materials Handbook and much more!