Characterizing Particles in Nano-Powder Regimes

February 1, 2001
/ Print / Reprints /
ShareMore
/ Text Size+
New high-resolution particle characterization methods have become available that allow accurate characterization of particles of ever decreasing size.



Nano-particles of increasingly smaller particle size and various material compositions are being developed for the pharmaceutical, biomedical, electronics, optoelectronics, energy, catalyst and ceramics industries. These particles are formed, or alternatively dispersed after formation, in a liquid medium, typically water. Various non-aqueous continuous media such as alcohols are also used.

The particle size and particle size distribution (PSD) of these materials are of great importance to the end user because they affect key colloid properties such as rheology, film gloss, surface area and packing density. Additionally, to prevent the aggregation of fine particles into much larger, undesirable units, steps must be taken to prevent particles from sticking together (aggregating) due to inter-particle collisions in the liquid medium. This can be accomplished by creating an interparticle electrical and/or steric energy barrier. For very fine particles, a combination of both electrical and steric barriers may be necessary to prevent aggregation.

The strength of the particle electrical barrier is measured in terms of an electrical potential termed the “zeta potential.” Zeta potential should be measured at process conditions, i.e., without prior sample dilution, as ions can adsorb or desorb from the particle surface upon dilution and change the zeta potential.

Until recently, those wishing to obtain zeta potential results had to resort to tedious and time-consuming “microelectrophoresis” methods that require extreme dilutions and consequently stringent sample handling precautions. As particle sizes decrease to the nanometer size range, the light scattering methods employed in microelectrophoresis become increasingly difficult to use due to extreme Doppler broadening of the scattered light from the fine particles. Thus, detectors must be placed very close to the incident laser beam direction, requiring superior mechanical and environmental stability.

However, a new instrument* is changing this process. Developed during the last 15 years, the instrument employs electroacoustic principles that provide accurate measurements while preventing the zeta potential probe from being susceptible to environmental noise or vibrations.

Zeta Potential Measurement in Action

The electroacoustic instrument measures the electrokinetic properties of a particle by an electroacoustic method. A high frequency electric field is applied to the dispersion, and the particles move electrophoretically in the applied field. If there is a density difference between the particle and the liquid, this motion will generate an alternating acoustic wave. The application of the electric field and the resulting acoustic wave provides a truly non-intrusive measurement and does not alter the properties of the sample.

Figure 1. Measured zeta potential and conductivity of an 8.3% wt titania slurry as a function of pH.
Tests were carried out on various materials to demonstrate the capabilities of the new instrument. Figure 1 shows the measured zeta potential of an 8.3% wt solids fine (~270 nanometer particle diameter) titanium dioxide system as a function of pH. The variation of electrical conductivity as a function of pH is also measured simultaneously during this automated “potentiometric titration.” This system has a zero of zeta potential (isoelectric point, IEP) at pH = 6.0. The location of the isoelectric point, in pH, is a characteristic of the particle surface and depends on the type of the metal oxide bond, the particle crystal structure, (rutile vs. anatase for titania) and on the type and level of impurities or other soluble species bonded to the titania particle surface.

Perhaps the single most important piece of information obtained from Figure 1 is that this titania system is unstable and will aggregate in the region of pH = 5 to pH = 7.3. This is because for particles in this size range (~270 nanometers), aggregation will occur in a concentrated system at a rapid rate for zeta potentials less than 20 millivolts in magnitude. For finer particles still, the zeta potential should be of even larger magnitude to prevent aggregation. In the extreme limit of very small nano-particles, sufficiently high zeta potentials cannot be achieved, and some level of steric stabilization is necessary.

The results shown in Figure 1 can be obtained in concentrated systems (in the range of 0.1 to 50 volume %) by carrying out automatic pH titrations in conjunction with a computer-controlled burette on a vigorously stirred and/or flowing sample. Measurements can be made every thirty seconds while accumulating about 60 data points over the whole pH range.

Figure 2. Zeta potential vs. pH of a very fine 10% wt silica system.
Figure 2 shows a potentiometric titration result on a 60-nanometer 10% wt silica particle system. For a pure silica surface, it is believed that the zeta potential approaches asymptotically an isoelectric point in the neighborhood of pH = 2.0. The Si – OH2+ configuration, implying a positive silica surface, is believed not to exist for the silica surface. This idea seems to be supported by the results of Figure 2. For this very fine particle system, it is estimated that the region of stability against aggregation would start from about pH = 7.0 and go higher in pH. Increasing pH much above 10 will again result in a decrease in the magnitude of the zeta potential due to compression of the electric double layer. This occurs as the ionic strength increases with pH. Thus, the stability region is restricted to pH higher than 7 for a very fine silica particle system.

The previous two examples display the utility of the zeta potential concept applied to particle stability considerations. Zeta potential measurements can also be used to determine the fractions of two different metals in mixed metal oxide catalyst particles, to determine the fraction of one crystal structure of a mixed structure metal oxide and many other applications too numerous to list here.

Figure 3. Particle size distributions from two mono-disperse latex and one broad silica particle systems.

Particle Size Distribution Data

Figure 3 shows superimposed high-resolution PSD results on two fairly monodispersed polystyrene latex systems and the silica system shown in Figure 2. The particle sizing instrument,** based on a patented capillary hydronamic fractionation (CHDF) technique, performs high-resolution particle sizing from 3 microns down to 10 nanometers.

Sample particles are fractionated according to size as they flow in a capillary tube. The particles are detected at the capillary outlet by an on-line detector, typically an ultraviolet (UV) detector. Particle size is given by the elution or transit time of the particles in the capillary. This elution time depends only on the particle hydrodynamic size and is independent of particle chemical composition and density.

True PSD data are produced in less than 10 minutes thanks to the high-resolution particle size fractionation capability of the CHDF technique. One significant CHDF advantage is that one can reliably measure PSD width and multimodality without the need for assumptions regarding the PSD shape.

The more traditional sizing methods employ laser light scattering by using either diffraction or photon correlation spectroscopy (PCS) techniques. Both are ensemble methods with inherently low resolution. As with any ensemble measurement, it is difficult to obtain reliable and consistent results for many particle systems, especially below about 100 nanometers in size, using these techniques. Ensemble measurements produce basically a mean particle size that can be fit by an infinite number of PSDs. This forces the software or instrument operator to guess a given PSD shape.

The importance of relying on true PSD data is illustrated as follows. Figure 3 samples Silica (blue) and Polysty1 (red) have the same mean particle size of 209 nm. This is unexpected given how dissimilar both samples’ PSDs are. Despite having identical weight-average particle size, these two samples will exhibit different properties, such as packing density, polishing capability, rheology, film gloss and surface area.

Another light diffraction disadvantage is that one needs to know the complex index of refraction (real and imaginary components of the index of refraction) for the particle material, and even then the particle surface morphology may play a surprising and hard to determine role.

New Particle Characterization Methods

As smaller-sized nano-particles are developed using a wider range of materials, particle characterization methods that require extreme dilutions and stringent sample handling precautions are quickly becoming outdated. Today, reliable and consistent results are critical to achieving a stable dispersion and a high-quality end product. New, rapid, easy to use, and high-resolution particle characterization methods have become available that meet these needs, allowing accurate characterization of particles of ever decreasing size.

For More Information

For more information about zeta potential measurement, contact Matec Applied Sciences, 56 Hudson St., Northborough, MA 01532; (508) 393-0155; fax (508) 393-5476; or visit http://www.matec.com.

*The ESA-9800 from Matec Applied Sciences, Northborough, Mass.
**The CHDF-2000 from Matec Applied Sciences

Did you enjoy this article? Click here to subscribe to Ceramic Industry Magazine.

You must login or register in order to post a comment.

Multimedia

Videos

Image Galleries

June 2014 Issue Highlights

Our June 2014 issue is now available!

Podcasts

Manufacturing Day 2014

Manufacturing Day organizers share their insights with Managing Editor Kelsey Seidler.

More Podcasts

Ceramic Industry Magazine

CI September 2014 cover

2014 September

You won't want to miss the CI Top 10, traditionally our most popular article of the year!

Table Of Contents Subscribe

THE CERAMIC INDUSTRY STORE

M:\General Shared\__AEC Store Katie Z\AEC Store\Images\Ceramics Industry\handbook of advanced ceramics.gif
Handbook of Advanced Ceramics Machining

Ceramics, with their unique properties and diverse applications, hold the potential to revolutionize many industries, including automotive and semiconductors.

More Products

Clear Seas Research

Clear Seas ResearchWith access to over one million professionals and more than 60 industry-specific publications,Clear Seas Research offers relevant insights from those who know your industry best. Let us customize a market research solution that exceeds your marketing goals.

Directories

CI Data Book July 2012

Ceramic Industry's Directories including Components, Equipment Digest, Services, Data Book & Buyers Guide, Materials Handbook and much more!

STAY CONNECTED

facebook_40px twitter_40px  youtube_40pxlinkedin_40google+ icon 40px