These materials offer greater strength and stiffness than their oxide counterparts, which means that less mass is required to support the same load. SiC-based materials also have high thermal conductivity, which, when combined with their lower mass, results in faster heating and reduced energy requirements. Finally, while oxide-based furniture tends to creep and warp, the SiC-based systems generally remain more rigid over a long period of high-temperature use. This is especially important in automated processes, which demand high tolerances for dimension, creep and warpage to ensure smooth operation. The higher durability of SiC kiln furniture also gives it greater longevity, enabling it to provide dramatic cost savings despite the increased initial investment required.
Recently, a new type of nitride-bonded SiC kiln furniture was developed that provides better oxidation resistance over a wide temperature range, increased coating life and fewer problems with sticking. With this new class of SiC kiln furniture, today’s ceramic manufacturers have an even broader range of low-mass kiln furniture options.
Recrystallized SiC kiln furniture is a pure SiC product with a maximum use temperature of 1650 degrees C.1 It is used in a broad range of applications in the form of posts, beams, rolls and flat shapes. However, due to its internal porosity, R-SiC can oxidize over long periods at elevated temperatures in oxidizing conditions.
Sintered SiC is the highest-strength SiC kiln furniture material on the market and resists oxidation up to temperatures of 1650 degrees C.2 It is typically offered in the form of beams and rolls. Its main disadvantage is its high initial cost.
Siliconized SiC is a dense, oxidation-resistant SiC product, in which the pores are filled with silicon.3 Its use is restricted to service temperatures below 1350 degrees C because silicon melts at ~1400 degrees C. Exceptionally strong and stiff, Si-SiC is valued for its load-bearing capacity, particularly in the form of beams and posts.
Nitride-bonded SiC kiln furniture is strong and fine-grained, and is typically supplied as flat shapes (setter plates), beams, posts and other shapes.4 It is used in a wide range of applications between 1200 and 1550 degrees C. Despite its fine microstructure, N-SiC resists oxidation because it is protected by a dense, passivating glassy layer. However, the material is limited to higher-temperature applications because the glassy layer breaks down at lower service temperatures (e.g., 800-1100 degrees C).
Figure 1 shows the strengths of each of these high-performance materials as a function of temperature.
New designs with the low-mass, high-strength benefits of SiC-based kiln furniture require less energy and can be cycled faster than oxide systems. N-SiC would be an attractive material for this application, but it is not appropriate for extended use at low service temperatures. Consequently, most roof tile manufacturers employ a combination of Si-SiC beams and oxide setter shapes.
The glassy passivating surface layer of N-SiC impedes the penetration of oxygen from the atmosphere to minimize the reaction with the SiC/Si3N4 in the bulk of the material. However, when the material is used solely at lower temperatures (<1200 degrees C), the silica layer is susceptible to damage, which leads to rapid oxidation and failure of the piece. The silica layer breaks down as a result of: 1) mechanical/handling damage, 2) cristobalite formation, and 3) bubbling of the silica layer.
Although handling damage is not frequently observed, it is a known cause of oxidation failure of N-SiC pieces. Manufacturers should ensure that parts are handled carefully. If damage occurs, the piece should be checked frequently to monitor degradation. For most high-service-temperature applications (>1200 degrees C), the protective glass layer typically “heals” itself, and the part will have a normal lifespan. Below 1200 degrees C, the glass has less of a tendency to heal and might fail early.
Cristobalite can form in the high-silica-content glassy layer and, with thermal cycling, can initiate and propagate cracks. This can make the silica layer ineffective at protecting the bulk of the kiln furniture from oxidation (see Figure 2).
In a similar way, oxidation of the bulk can occur when the glass layer breaks down due to the formation of bubbles in the glass (see Figure 3). When the bubbles grow and burst, the openings left behind allow air to penetrate the microstructure and rapidly oxidize the part. Research has shown that bubbles are typically found in service conditions with high humidity. This is due to the following reaction sequence:
SiC + 2H2O - SiO2 + C + 2H2
2C + O2 - 2CO
This reaction sequence produces more gas than is taken in during the reaction. Due to the low solubility of CO in the glass, bubbles can form, grow and ultimately burst. Above 1200 degrees C, the bubbles are smaller, and the gas is released quickly. At lower temperatures, the higher glass viscosity results in larger bubbles, which collapse and leave the bulk material unprotected.
In each case of silica layer breakdown, the damage normally re-heals under oxidizing conditions above 1200 degrees C. However, at lower application temperatures, the passivating layer cannot re-heal due to the high glass viscosity and slow oxidation kinetics. As a result, bulk oxidation is allowed to continue locally. Over a short period of time, the internal oxidation can lead to cracks and warpage, which further accelerate the part’s failure.
One type of kiln furniture made with this material performs well over a wide range of service conditions.5 It is comparable in strength and stiffness to other N-SiC materials, but it can withstand low-temperature degradation of the passivating layer due to its unique nature. The new material also enhances the life of applied coatings (compared to conventional N-SiC) and reduces sticking at elevated temperatures (up to 1550 degrees C).
Another type of kiln furniture made with the new N-SiC material exhibits the best results in low temperature oxidation.6 Targeted for low-temperature (<1200 degrees C) service conditions only, it enables the use of N-SiC products over the entire 800-1550 degrees C temperature range.
Roof Tile. The low-temperature oxidation resistance of the new N-SiC kiln furniture makes it ideal for use in roof tile kilns, where kiln furniture must be oxidation-resistant at low service temperatures, as well as resistant to bubbling resulting from the high humidity typical in the firing of clay-based roof tiles.
In one test, flat shapes of the new kiln furniture were cycled for more than 12 months in a European roof tile kiln without any sign of degradation or bulk oxidation. In a second trial, beams were cycled in a roof tile kiln for more than 11 months (as of June 2003) without any signs of damage.
Porcelain. One form of the new N-SiC kiln furniture is stable in both low- and high-temperature environments.5 Due to a surface that is rougher than most fine N-SiC materials, it also offers advantages of increased coating life and reduced sticking, particularly in applications where elevated temperatures normally cause a buildup of glass.
At a porcelain manufacturing site with an application temperature of ~1400 degrees C, the coating life on setters made with the new N-SiC material was improved by about 30 percent compared to similarly coated conventional N-SiC setters. Product performance was also comparable to conventional N-SiC when used for extended periods.
Advanced Ceramics. The combined high- and low-temperature oxidation resistance of the new N-SiC material makes it especially attractive for use as posts in applications with a range of temperatures—such as when one end is cemented into an insulated base while the other end experiences the normal firing temperatures of the kiln.
This type of application would normally pose a problem for high-service-temperature kilns (e.g., >1350 degrees C) where Si-SiC kiln furniture cannot be used, and where conventional N-SiC furniture can suffer from oxidation damage near the insulated bottom of the post. The new N-SiC material operates well in both environments, making it an ideal choice for this application. Tests of posts made with the new N-SiC material have been in progress for more than 12 months (as of June 2003) with good performance to date.
With the recent development of a new N-SiC kiln furniture material, companies can enjoy the benefits of higher-performing, low-mass SiC kiln furniture in almost any firing application.
2. Hexoloy SA, a registered trademark of Saint-Gobain Industrial Ceramics, is an example of S-SiC.
3. Silit SK, a registered trademark of Saint-Gobain Industrial Ceramics, is an example of Si-SiC.
4. Advancer, a registered trademark of Saint-Gobain Industrial Ceramics, is an example of high-temperature N-SiC.
5. Annasicon RTH (patent pending), developed and supplied by Saint-Gobain Industrial Ceramics.
6. Annasicon RT (patent pending), developed and supplied by Saint-Gobain Industrial Ceramics.